Formation of nanometer-sized Cu-Sn-Se particles in Cu2ZnSnSe4 thin-films and their effect on solar cell efficiency

in ACTA MATERIALIA (2017), 132

Atom probe tomography and transmission electron microscopy are used to study the formation of nano sized Cu-Sn-Se particles in Cu2ZnSnSe4 thin -films. For a Cu -rich precursor, which was deposited at 320 ... [more ▼]

Atom probe tomography and transmission electron microscopy are used to study the formation of nano sized Cu-Sn-Se particles in Cu2ZnSnSe4 thin -films. For a Cu -rich precursor, which was deposited at 320 degrees C under Cu- and Zn-rich growth conditions, Cu2-xSe grains at the surface are detected. During annealing the precursor at 500 degrees C in a SnSe + Se atmosphere most of the Cu2-xSe is transformed to Cu2ZnSnSe4 via the consumption of excessive ZnSe and incorporation of Sn. However, atom probe tomography studies also reveal the formation of various nanometer-sized Cu-Sn-Se particles close to the CdS/Cu(2)ZnSnSe4 interface. One of those particles has a composition close to the Cu2SnSe3 compound. This phase has a smaller band gap than Cu2ZnSnSe4 and is proposed to lead to a significant drop in the open -circuit voltage and could be the main cause for a detrimental p-n junction and the zero efficiency of the final device. Possible effects of the other phases on solar cell performance and formation mechanisms are discussed as well. (C)2017 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved. [less ▲]